Effect of superabsorbent polymer and polypropylene fiber on mechanical performances of alkali-activated high-calcium fly ash mortar under ambient and elevated temperatures

Journal article

Authors/Editors

WEERACHART TANGCHIRAPAT

Strategic Research Themes

Innovative Materials, Manufacturing and Construction (Strategic Research Themes)

Publication Details

Author list: Chindasiriphan, Pattharaphon; Nuaklong, Peem; Keawsawasvong, Suraparb; Thongchom, Chanachai; Jirawattanasomkul, Tidarut; Jongvivatsakul, Pitcha; Tangchirapat, Weerachart; Likitlersuang, Suched;

Publisher: Elsevier

Publication year: 2023

Volume number: 71

ISSN: 23527102

eISSN: 2352-7102

URL: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85154063756&doi=10.1016%2fj.jobe.2023.106509&partnerID=40&md5=dcf23c85e154d233f3e8d30b81e0372e

Languages: English-Great Britain (EN-GB)

View in Web of Science | View on publisher site | View citing articles in Web of Science

Abstract

This study investigated the mechanical properties of alkali-activated fly ash (AAF) mortars containing superabsorbent polymers (SAPs) and polypropylene (PP) fibers before and after exposure to elevated temperatures. AAF mortars were synthesized using sodium silicate and high-calcium fly ash as the solid activator and aluminosilicate source, respectively. This procedure classified the binder as a one-part AAF mortar. The mechanical properties of the AAF mortar, including compressive and flexural strengths, were investigated considering eight mixes with varying SAP contents (0%, 0.5%, 1%, and 2% by weight of binder) and fiber contents (0 and 0.2% by volume). Moreover, physical properties including the permeability and sorptivity were examined, and physiochemical analysis was performed to evaluate the behavior of AAF mortar at room temperature, 300, 500, and 700 °C. The results show that the compressive strength of specimens at room temperature slightly decreased owing to the increased macroporosity caused by SAPs through pre-swelling, while the flexural strength was maintained via an internal curing effect. The PP fibers significantly enhanced the flexural capacity of the cement mortar, while the compressive strength initially decreased at 28 d and later exhibited a negligible effect at 90 d. The specimens produced using SAPs were effective in preserving the residual compressive and flexural strengths compared with those without SAPs after exposure to 300 °C. Meanwhile, the residual strength of PP fiber specimens diminished after elevated temperature exposure because the melted fiber led to the excessive formation of cavities. © 2023 Elsevier Ltd

Keywords

Alkali-activation, Superabsorbent polymer