Effect of alloying element antimony on macrostructural and microstructural development in A356 alloy directionally solidified under unsteady-state conditions

Journal article

Authors/Editors

Strategic Research Themes

No matching items found.

Publication Details

Author list: Boontein S., Kajornchaiyakul J., Limmaneevichitr C.

Publisher: Elsevier

Publication year: 2008

Journal: Journal of Materials Science & Technology (1005-0302)

Volume number: 24

Issue number: 1

Start page: 25

End page: 28

Number of pages: 4

ISSN: 1005-0302

URL: https://www.scopus.com/inward/record.uri?eid=2-s2.0-40449142229&partnerID=40&md5=9bc24a3d669c2e979c35b3c25f1dbee4

Languages: English-Great Britain (EN-GB)

View in Web of Science | View citing articles in Web of Science

Abstract

Microstructure development is well accepted to have a major effect on mechanical properties during its services. One of the most interesting ways to improve mechanical properties is to reduce secondary dendrite arm spacing (SDAS). SDAS also plays an important role in controlling and providing the well distributed and fine microstructure resulting in better tensile strength and elongation. To reduce SDAS, it is commonly known by increasing cooling rate and increasing interface instability by limited-soluble alloy addition. It is, however, unclear that how both cooling rate and limited-soluble alloy, e.g. Sb, relate to each other. This may be the reason that the limited-soluble alloy may not effectively reduce SDAS. To better understand this phenomenon, influences of Sb on solid/liquid interface instability using columnar to equiaxed transition (CET) were studied in the directionally solidification experiment. From macrographs and micrographs, it was observed that at 0.06-0.18 wt pct Sb the CET min, CET max, CET zone and %CET area gradually increased. The increases of CET max and CET zone in samples with 0.06 to 0.18 wt pct Sb addition results from recalesced zone. On the other hand, the variations of CET max and CET zone in samples with 0.24 to 0.30 wt pct Sb results from equiaxed grain formations that prohibit the growth of columnar grain and latent heat from intermetallic phase solidified.

Keywords

Al-Si alloy, Antimony, Directional solidification