Mechanical properties at high temperatures and microstructures of a nickel aluminum bronze alloy

Conference proceedings article

ผู้เขียน/บรรณาธิการ

กลุ่มสาขาการวิจัยเชิงกลยุทธ์

ไม่พบข้อมูลที่เกี่ยวข้อง

รายละเอียดสำหรับงานพิมพ์

รายชื่อผู้แต่ง: Thossatheppitak B., Suranuntchai S., Uthaisangsuk V., Manonukul A., Mungsuntisuk P.

ผู้เผยแพร่: Trans Tech Publications

ปีที่เผยแพร่ (ค.ศ.): 2013

Volume number: 683

หน้าแรก: 82

หน้าสุดท้าย: 89

จำนวนหน้า: 8

ISBN: 9783037856666

นอก: 1022-6680

eISSN: 1662-8985

URL: https://www.scopus.com/inward/record.uri?eid=2-s2.0-84878325817&doi=10.4028%2fwww.scientific.net%2fAMR.683.82&partnerID=40&md5=017d9ccc82674ec33a0091b598951866

ภาษา: English-Great Britain (EN-GB)

ดูในเว็บของวิทยาศาสตร์ | ดูบนเว็บไซต์ของสำนักพิมพ์ | บทความในเว็บของวิทยาศาสตร์

บทคัดย่อ

Nickel Aluminum Bronze (NAB) alloys have been widely used in different kinds of machine parts where the superior resistance to corrosion and erosion in saltwater is needed. In this work, mechanical properties at high temperatures and microstructures of a NAB alloy were investigated. First, NAB specimens were prepared as an as-cast ingot and were subsequently heattreated at 675ฐC for 6 hours in order to improve microstructure and mechanical properties. The mechanical properties at high temperatures in form of the plastic flow curves of the NAB alloy were characterized by a deformation dilatometer. The NAB samples were compressed at high temperature and rapidly cooled down to room temperature. The deformation temperatures of 825ฐC, 850ฐC and 900ฐC, a strain rate of 0.01 s-1, and a maximum compression strain of 0.4 were considered. The influences of the temperature on flow behavior of the NAB alloy were investigated. The plastic stress-strain curves at different temperatures were compared with regard to the rate of material strain hardening and softening. It was found that the compression stresses decreased with increasing temperatures. Additionally, the resulted hardness and microstructures of the alloy after forming at high temperatures were analyzed. ฉ (2013) Trans Tech Publications, Switzerland.

คำสำคัญ

Grain size, Hot compression, Nickel aluminum bronze, Plastic stress-strain curves